PS Base with Aluminum Fabrication Steps
Printing PS version of the base method for producing aluminum sheet, characterized in that it is the method steps:
A. according to the parts by weight ratio of Al: 98, Si: <1.0, Fe: 0.3 ~ 1.0, Cu: 0.03, Zn: 0.03, Mg: 0.03, Ti: 0.05 ratio will be above the melting temperature of the alloy composition after mixing 720 - under the conditions of 800 ℃ melting;
B. then for the next casting temperature condition of 690 ~ 750 ℃ alloy casting into ingot;
C. alloy ingot to make the ingot at a temperature of 500 ~ 610 ℃ conditions homogenization;
D. then subjected to hot rolling at a temperature of 400 ~ 540 ℃ temperature;
E. hot-rolled material consisting of 9.0mm cold-rolled to 0.7mm;
F. at a temperature of 300 ℃ ~ 500 ℃ conditions of intermediate annealing 11h, insulation 1h then cold rolling to 0.15mm, stretched, fully straightening, after cutting to be finished.
- 2000 series Aluminium sheet Alloy:2014/2017/2024/2124/2219 Temper:O,T3,T361,T4,T451,T6,T81,T851,T86
- 2000 series Aluminium sheet:2014,2017,2024,2124,2219 aluminium sheet,temper:O,T3,T4,T451,T351,T361,T6,T81,T86,T651,T851,T86,T31,T62,T87,2000 aluminium sheet is W...
- 1000 series Aluminum circle/aluminum discs Alloy:AA1050,AA1060,AA1100
- 1000 Aluminum Circle Including:1050 aluminium circle sheet,1060 aluminium disk,1070 aluminium round sheet,1100 aluminium discs,1200 aluminium circle.,It is mainl...
- Architectural aluminum cladding perforated panels
- Architectural aluminum cladding perforated panels Application:For the curtain wall, both outer-side and inner side/Ceiling/Underground/Airport/Bus station/Railwa...
- 5000 series 5-bar Aluminum Tread Plate Alloy:5005/5052/5083/5754/5086/5182/5A02 Temper:O,H114,H22
- The major series of this series aluminum tread plate provided by Mintai includes 5005 5052 5083 5086 5154 5182 5251 5754 series etc. aluminum tread plate used as...